KLJ Group is the top manufacturer of Plasticizers & Compounds and also a trading firm dealing in various products. KLJ is energetically developing a variety of new products, grades, processes, applications and achieving new limits in quality to really meet the customer needs and to stay ahead of the competition.

KLJ Group also manufactures Plastic Compound such as PVC Compounds for footwears, automobile industries, cable industries, NBR Compounds for telephone and automobile industries, TPR Compounds for unit soles & sports shoes, PVC master Batches for cables & footwears, blending of various polymers with PVC, etc.

We have been recently added to the KLJ portfolios phosphate esters such as Tricresyl phosphate, Tributyl phosphate etc.

Plants at Silvassa and Barucha have been certified for ISO 9001 : 2000 and ISO 14001

 
Product Specifications...
PLASTICIZERS
PRODUCT SPECIFI-CATION TEST METHOD DI-2ETHYL
HEXYL
PHTHA-LATE
DOP		 DI-BUTYL PHTHA-LATE
DBP(M)		 DI-ISO-BUTYL PHTHAL-ATE
DIBP		 DI-ISO-DECYL PHTHA-LATE
DIDP		 DI-ISO-NONYL PHTHA-LATE
DINP		 DI-n-BUTYL PHTHALATE
D-n-BP		 DI-ETHYL PHTHALATE
DEP		 DI-METHYL PHTHALATE
DMP
APPEARANCE PHYSICAL   WATER WHITE CLEAR LIQUID
COLOUR IN 
MAX HAZEN UNIT		 ASTM-D-1045-86 30 30 30 40 30 30 20 20
VOLATILE
LOSS (130°C for 3 hrs. % 
By Mass) 
Max.		 KLJTM-P-11-92 0.1 0.1 (110°C for 2 Hrs.) 0.1 (110°C for 2 Hrs.) 0.1 0.1 0.1 (110°C for 2 Hrs.) 0.2(110°C for 1 Hour) 0.5(110°C for 1 Hour)
ACIDITY % 
(AS ACID) 
BY MASS, 
Max.		 ASTM-D-1045-86 0.01 0.01 0.01 0.01 0.01 0.01 0.015 0.02
ACIDITY
AFTER HEAT TREATMENTS 80°C for 
2 Hrs.) % By Mass, Max.		 ISI-9591-96 0.03 0.03 0.03 0.03 0.03 0.03 0.05 0.05
HEAT STABILITY AT180°C
for2Hrs.		 ISI-9591-96 NO CHANGE IN COLOUR NO CHANGE IN COLOUR NO CHANGE
IN COLOUR
(150°C, 2 Hrs.)		 NO CHANGE IN COLOUR NO CHANGE IN COLOUR NO CHANGE
IN COLOUR
(150°C,2Hrs.)		 50 Hu. (150°C,2Hrs.) 50 Hu. (150°C,2Hrs.)
SPECIFIC GRAVITY 
AT 27° C		 ASTM-D-1045-86 0.983 ±0.003 1.04 ±0.001 1.035 ±0.005 0.967 ±0.004 0.973 ±0.003 1.043 ±0.002 1.117±0.003 1.185 ±0.005
REFRACTIVE INDEX 
AT 27° C		 ASTM-D-1045-86 1.486 ±0.002 1.492 ±0.003 1.492 ±0.003 1.4845 ±0.0015 1.487±0.002 1.4845 ±0.0015 1.507± 0.002 1.512 ±0.004
ESTER VALUE (mg KOH/gm) ASTM-D-1045-86 287 ±3 385 ±9 402 ±3 251.5±2.5 267.5±2.5 403 ±3 503 ±3 575 ±3
ESTER CONTENT % BY WEIGHT, Min. ASTM-D-1045-86 99.5 99.5 99.5 99.5 99.5 99.5 99.5 99.5
PLASTICIZING ESTERS 
BY GLC 
Min. %		 KLJTM-P-12-98 99.5 99.5 99.5 99.5 99.5 99.5 99.5 99.5
MOISTURE 
% BY MASS Max.		 ASTM-E-203 0.1 0 0.1 0.1 0.1 0.1 0.2 0.4
VISCOSITY 
AT 20°
CINCPS		 KLJTM-P-13-97 82 ±2 23 ±2 34.5±1.5 108 ±2 79 ±3 21 ±2 12 ± 2 -
BOILING AT ATM. PR
. (In °C) IODINE 
VALUE MAXIMUM		 IS:5298-73
BRITISH-
PHARM.-88		 386 - 327 - 400 340 293 -
top
APPLICATIONS:
Footwear * Cables & Flexible PVC Films * Leather Cloth * Vinyl Flooring * Medical Equipments * Nontoxic food containers * Adhesives * Perfumes * Automobile Parts * Rubber belts * Tubes etc.
Specifications are indicative with no binding on KLJ Group.
 
PLASTICIZERS
PRODUCT SPECIFICATION> TEST METHOD> DI-OCTYL MALEATE
DOM>		 DI-n-BUTYL MALEATE
DBM>		 n-BUTYL STEARATE
nBS>		 OCTYL STEARATE
OS>		 DI-OCTYL AD I PATE
DOA>		 TRI-OCTYL TRIMELLITATE
TOTM>		 BENZYL
BUTYL
PHTHALATE
BBP>		 BUTYL
OCTYL
PHTHALATE
BOP>
APPEARANCE> PHYSICAL>  > WATER WHITE CLEAR LIQUID>  > OFF WHITE CLEAR LIQUID>
COLOUR IN MAX HAZEN UNIT> ASTM-D-1045-86> 40> 40> 60> 60> 30> 50> 100> 50>
VOLATILE LOSS (130°C for 3 hrs. % By Mass) Max.> KLJTM-P-11-92> 0.2> 0.5(110°C for 2 Hrs.)> 0.2(110°C for 2 Hrs.)> 0.2> 0.2> 0.1> 0.1> 0.1>
ACIDITY % (AS ACID) BY MASS, Max.> ASTM-D-1045-86> 0.02> 0.02> 0.2> 0.5> 0.03> 0.03> 0.02> 0.15>
ACIDITY AFTER HEAT TREATMENTS 80°C for 2 Hrs.) % By Mass, Max.> ISI-9591-96> 0.03> 0.05> N.A.> N.A.> 0.03> 0.03> 0.04> 0.03>
HEAT STABILITY AT180°Cfor2Hrs.> ISI-9591-96> 50 HU> 50 HU> NO CHANGE IN COLOUR> NO CHANGE IN COLOUR> 50 HU> 50 HU> 150 HU> 100 HU>
SPECIFIC GRAVITY AT 27° C> ASTM-D-1045-86> 0.943 ±0.003> 0.988 ±0.003> 0.955 ±0.005> 0.860 ±0.005> 0.924 ±0.002> 0.990 ±0.005> 0.561 ±0.556> 0.495 ±0.490>
REFRACTIVE INDEX AT 27° C> ASTM-D-1045-86> 1.450 ±0.006> 1.450 ±0.006> 1.445 ±0.005> 1.455 ±0.005> 1.448 ±0.001> 1.4860 ±0.0013> 1.538 ±0.004> ->
ESTER VALUE (mg KOH/gm)> ASTM-D-1045-86> 330 ±3> 492.5 ±2.5> 162.5 ±2.5> 142.5 ±2.5> 304 ±1> 306.5 ±3.5> 358 ±5> 335 ±5>
ESTER CONTENT % BY WEIGHT, Min.> ASTM-D-1045-86> 99> 99> 99.5> 99.5> 99.5> 99> 99> 99>
PLASTICIZING ESTERS BY GLC Min. %> KLJTM-P-12-98> 99> 99> 99> 99> 99.5> 99> 99> 99>
MOISTURE % BY MASS Max.> ASTM-E-203> 0.1> 0.1> 0.1> 0.1> 0.1> 0.1> 0.1> ->
VISCOSITY AT 20°CINCPS> KLJTM-P-13-97> 19.5 ± 1.5> 8±2> 10-12 (at 25°C)> 18-20 (at 25°C)> 14±2> 274.5 ±2.5> 66 ±2> ->
BOILING AT ATM. PR. (In CC) IODINE VALUE MAXIMUM> IS:5298-73
BRITISH-
PHARM.-88>		 -> 280.6> 2.5 PPM> 2.5 PPM> 335> -> 370> ->
top
n-BUTYL STEARATE
APPLICATION>
  • Processing PVC rigid pipes & profiles.
  • Plastisol
  • Polystyrene and ABS
  • PVC Leather Cloth, Vinyl Flooring & Films.
  • Wetting agent for PVC/PE/PS.
  • PVC Footwear.
  • Flexible PVC Tubing & Pipe.
  • PVC Compounds for various applications.>
    		•
    SPECIFICATIONS> Appearance                     :                 Clear Liquid
    Iodine Value                    :                 2.5 Max.
    Volatile loss                    :                 0.20% Max.
    (110°Cfor2Hrs.)
    Acid Value                       :                 1.0 Max
    (MgsKOH/Gm)
    Heat Stability                   :                 No change
    (180°C/2Hrs.)
    Specific Gravity                :                 0.85-0.86
    (at27°C)
    Refractive Index               :                 1.440-1.450
    (at27°C)
    Purity by G.C.                   :                 99.0 Min.
    Moisture by Mass              :                 0.10% Max.
    Viscosity (at 25°C)                              10 to 12 Cp.>
    top
    CHLORINATED PARAFFIN (CP)
    top
    PHOSPATE ESTERS
    top
    PVC FOOTWEAR COMPOUNDS
    TYPICAL
    PROPERTIES    		 SPECIFIC
    GRAVITY    		 HARDNESS THERMAL
    STABILITY    		 VOLATILE
    LOSSAT130°C    		 TENSILE
    STRENGTH

    MODULUS AT
    100% ELONGATION

    		 ELONGATION
    AT BREAK
    GRADE/UNIT     (±0.02) Shore A (±0.2) MIN. (±0.2)   (±0.2) kg/cm2 (±15)   (±5) % (±10%)
    MICRO CELLULARBM-55 (After Expn.)0.49 (After Expn.)AE22 23 1.01 23 - 335
    COMPACT              
    BT-60 1.18 60 30 0.09 128 40 450
    Q3 1.24 60 33 6.09 115 36 460
    R4 1.27 70 12 5.37 170 65 360
    S-3 1.3 70 13 2.93 130 42 500
    TRANSPARENT              
    AST-2 1.25 65 18 5.61 130 60 295
    TPR COMPOUND              
    TPR-U-50* (43) 0.96 50      ' - - 40 - 450
    top
    * Mil 60±5gm/ 10cm.
    Ross Flex cut growth (150000 cycles) < 6mm.
    Specifications are indicative with no binding on KLJ Group
     
    PVC COMPOUNDS FOR SPECIALITY MOULDING / EXTRUSION
    TYPICAL PROPERTIES SPECIFIC GRAVITY HARDNESS THERMAL STABILITY VOLATILE
    LOSSAT130°C    		 TENSILESTRENGTH MODULUS AT
    100%ELONGATION    		 ELONGATIONAT BREAK BROAD APPLICATIONS
    GRADE
    /UNIT    		 (±0.02) Shore A (±0.2) MINI.
    (±1)    		 (±0.02) kg/cm2 (±15) (±15) % (±10%)  
    Q3 1.24 60 33 6.09 115 36 460

    General profile extrusion & injection moulded component e.g.-handle grips
    RO 1.12 40 6 5.08 70 20 400

    Small moulded components
    R2 1.24 50 6 5.01 77 28 340

    Small moulded components
    S5 13 70 9 4.28 150 45 250

    Car foot mats, mud flaps & door trims
    SG22 1.25 30 9 4.5 45 20 420

    Handle grips, sleevings
    BR6 1.17 55 25 5.01 103 35 430